would u like to know the development trend of steel industry on Chinafirebrick?

ChangXing Refractory is a Chinese leading refractory and oil fracturing proppant manufacturer & supplier with a wide range industries in high temperature.The volume of refractories consumed is projected to rise in the USA, Western Europe, and Japan following an extended period of decline, as economic conditions strengthen in these areas and output of ferrous metals and other refractories-using products rebounds. Output gains in these areas are more likely to result in higher refractories demand because the manufacturing techniques used are already so efficient that it will be much difficult to reduce refractories consumption on a per unit output basis than in less developed countries. Due to their greater use of more costly, high-quality products, the US, Western Europe, and Japan will account for a larger share of the world refractories market in dollar terms in 2020 than they will in tonnage.

The world average consumption of refractories per tonne crude steel was 15 kg/t in 2014, while China‘s average was 20 kg/t. The growing demand for refractories in the Asia-Pacific region is the major driving factor of the market. Twenty years ago, glass consumed 11–13 kg/t of refractories, a figure that has dropped to 4,5–5,5 kg/t today. Steel, on the other hand, has reduced consumption from 30 kg/t in 1980 to 10 kg/t today. Strong growth in emerging markets is the main driving force for the refractories market. In addition, high demand from the glass industry is also expected.
Globally glass industry consumes 0,75–1 Mt/a of refractories, far less than steel. The demand for higher-performance refractories such as magnesia-zircon is increasing. Over 95 % of refractories used in the glass industry are shaped. Monolithics are used in combination with shapes. Environmental concerns prove to be the major restraint for the refractories market. Moreover, because of moderation in raw material costs and refractories prices, growth is restricted.
Lastly, the report is divided by geography – North America, Europe, Asia-Pacific (APAC), South America and Middle-East and Africa (MEA); where in the market share of each region is analyzed and estimates are provided for the next 6 years.Chinafirebrick provides refractory products, calcium silicate products, castable & mortar,fire brick, ladle & tundish nozzle, ceramic fiber with high quality for you.

why not know the development trend of China refractory on Chinafirebrick?

ChangXing Refractory is a Chinese leading refractory and oil fracturing proppant manufacturer & supplier with a wide range industries in high temperature field . From a refractory bricks manufacturing factory, Changxing has become a professional manufacture with various refractory materials and oil fracturing proppant both in domestic and international market during 30+ years, whose customers covering North America, Middle East, South Asia, Africa, etc.Would u like to know more refractory material information ?come on.
ReportsnReports.com adds 134 pages refractory material industry research report on global and Chinese markets, published in September 2014, to its online business intelligence library. Refractory material is one of the indispensible materials in such high-temperature industries as iron and steel, building materials, chemicals, nonferrous metals, etc. Over 70% of refractory materials worldwide are applied in iron and steel smelting, 17% in building material industry and 4% in chemical industry.
Global refractories market is currently valued at USD 40,9 billion in 2014 and is expected to reach USD 54,8 billion by 2020, showing a Compound Annual Growth Rate (CAGR) of 5 %.
In terms of tonnage, the global market was at 39,8 Mt/a in 2014 and is expected to reach 48,6 Mt by 2020. China will maintain its top position among countries, with a market share of more than 50 % in the refractories market. The gains registered in recent years because of a moderation in raw material costs and refractories prices were not as strong. The iron and steel market will reportedly continue to dominate global refractories sales, accounting for more than three-fifths of all 2020 product-demand in volume terms.
The report elucidates the situation of refractories around the world and studies its markets by end-user industry, which include iron and steel, energy and chemicals, nonferrous metals, cement, ceramics, glass and others; and by product type: magnesite and chrome, zircon and zirconia, silicon carbide, graphite and carbon, high-alumina and fireclay among others. Chinafirebrick provides refractory products, calcium silicate products, refractory castable & mortar, fire brick, ladle & tundish nozzle, ceramic fiber with high quality for you.

would u like to know more refractory products information on Chinafirebrick?

Refractories are heat resistant materials that provide the linings for high-temperature furnaces, reactors, and other processing units.ChangXing Refractory is a Chinese leading refractory and oil fracturing proppant manufacturer & supplier with a wide range industries in high temperature field . From a refractory bricks manufacturing factory, Changxing has become a professional manufacture with various refractory materials and oil fracturing proppant both in domestic and international market during 30+ years, whose customers covering North America, Middle East, South Asia, Africa, etc.
The Refractory Ceramics Division of Ceramic Society examines the science, production and application of ceramics for use at elevated temperatures and in other hostile environments. Members are involved in materials development, formulation, production, and engineering of refractories for the iron, steel, aluminum, and other nonferrous metal industries as well as the minerals processing, glass, cement, and petrochemical industries.
Development of global refractory material industry; Policy and industry environment of Chinese refractory material industry; Markey supply & demand, competitive landscape, etc. of Chinese refractory material market; Development and major companies of refractory product segments such as basic refractory materials, unshaped refractory materials, ceramic fiber, etc.; Upstream/downstream refractory material market analysis; Operation and refractory material business analysis of 7 key refractory material companies in the world and 8 ones in China. China is the largest producer and exporter of refractory materials around the globe. In 2013, China's refractory material output hit 28.189 million tons, sweeping more than 66% of the world's total; export volume topped 1.769 million tons, 51.7 times the import volume.
Despite the global leading position, Chinese refractory materials have been confronted with the prominent problem of overcapacity in recent years. Additionally, subject to growth slowdown in downstream sectors, the falling demand and other factors, market competition intensifies. Enterprises in the field received reduced orders and saw sales volume in decline, some companies even in the red.whatever,if u need any refracotry products , you can contact us.Our website is http://www.chinafirebrick.com/.

Refractory Materials Design for Rotary Cement Kiln -- Changxing Refractory

With 30 years development and rich work site construction experience, Changxing Refractory has accumulated enough experience in supplying materials for rotary cement kiln. Sum up, we have the following points to share.
1. There are two types of rotary cement kiln. One is wet process kiln, used for cement production, chemical industry, and metallurgy. The other type is dry process kiln, all used for producing Cement, lime, alumina, aluminum hydroxide, carbon, etc.
2. Due to raw material temperature change along furnace length, the furnace consist of 6 zones: Drying zone(<150 ℃), preheating zone(150-750 ℃), calcining zone(750-1000 ℃), exothermic reaction zone(1000-1300 ℃), firing zone(1300-1400 ℃), cooling zone(1300-1000 ℃).

3. Brief refractory materials design for each part of rotary cement kiln.

A. For center part of firing zone: Direct bonded magnesia chrome brick of common magnesia chrome brick (Refractoriness under load: min 1700 ℃).
B. For transitional zone: Spinel brick, silica mullite brick.
C. For kiln discharging mouth: SIC brick, spinel brick, direct-bonded magnesia chrome brick and castable.
D. For kiln mouth: High quality high alumina brick, phosphate bonded high alumina brick.
E. For Kiln door: High alumina brick, clay insulation brick and calcium silicate board, etc.
F. For cooling zone: Anti-alkali brick and castable.

Generally, Changxing Refractory can offer clients with free customized design and give clients a competitive cost budget to improve cement productivity, and also, Changxing Refractory can dispatch engineers for work site guidance. Should you have any needs of the whole program design and refractory materials supply, please feel free to contact us, we warmly welcome any questions and inquiry.
The link :http://www.chinafirebrick.com/Company_News_40.html

Refractory Materials Design for Rotary Cement Kiln -- Changxing Refractory

With 30 years development and rich work site construction experience, Changxing Refractory has accumulated enough experience in supplying materials for rotary cement kiln. Sum up, we have the following points to share.
1. There are two types of rotary cement kiln. One is wet process kiln, used for cement production, chemical industry, and metallurgy. The other type is dry process kiln, all used for producing Cement, lime, alumina, aluminum hydroxide, carbon, etc.
2. Due to raw material temperature change along furnace length, the furnace consist of 6 zones: Drying zone(<150 ℃), preheating zone(150-750 ℃), calcining zone(750-1000 ℃), exothermic reaction zone(1000-1300 ℃), firing zone(1300-1400 ℃), cooling zone(1300-1000 ℃).

3. Brief refractory materials design for each part of rotary cement kiln.

A. For center part of firing zone: Direct bonded magnesia chrome brick of common magnesia chrome brick (Refractoriness under load: min 1700 ℃).
B. For transitional zone: Spinel brick, silica mullite brick.
C. For kiln discharging mouth: SIC brick, spinel brick, direct-bonded magnesia chrome brick and castable.
D. For kiln mouth: High quality high alumina brick, phosphate bonded high alumina brick.
E. For Kiln door: High alumina brick, clay insulation brick and calcium silicate board, etc.
F. For cooling zone: Anti-alkali brick and castable.

Generally, Changxing Refractory can offer clients with free customized design and give clients a competitive cost budget to improve cement productivity, and also, Changxing Refractory can dispatch engineers for work site guidance. Should you have any needs of the whole program design and refractory materials supply, please feel free to contact us, we warmly welcome any questions and inquiry.
The link :http://www.chinafirebrick.com/Company_News_40.html

Refractory Materials Design for Rotary Cement Kiln -- Changxing Refractory

With 30 years development and rich work site construction experience, Changxing Refractory has accumulated enough experience in supplying materials for rotary cement kiln. Sum up, we have the following points to share.
1. There are two types of rotary cement kiln. One is wet process kiln, used for cement production, chemical industry, and metallurgy. The other type is dry process kiln, all used for producing Cement, lime, alumina, aluminum hydroxide, carbon, etc.
2. Due to raw material temperature change along furnace length, the furnace consist of 6 zones: Drying zone(<150 ℃), preheating zone(150-750 ℃), calcining zone(750-1000 ℃), exothermic reaction zone(1000-1300 ℃), firing zone(1300-1400 ℃), cooling zone(1300-1000 ℃).

3. Brief refractory materials design for each part of rotary cement kiln.

A. For center part of firing zone: Direct bonded magnesia chrome brick of common magnesia chrome brick (Refractoriness under load: min 1700 ℃).
B. For transitional zone: Spinel brick, silica mullite brick.
C. For kiln discharging mouth: SIC brick, spinel brick, direct-bonded magnesia chrome brick and castable.
D. For kiln mouth: High quality high alumina brick, phosphate bonded high alumina brick.
E. For Kiln door: High alumina brick, clay insulation brick and calcium silicate board, etc.
F. For cooling zone: Anti-alkali brick and castable.

Generally, Changxing Refractory can offer clients with free customized design and give clients a competitive cost budget to improve cement productivity, and also, Changxing Refractory can dispatch engineers for work site guidance. Should you have any needs of the whole program design and refractory materials supply, please feel free to contact us, we warmly welcome any questions and inquiry.
The link :http://www.chinafirebrick.com/Company_News_40.html

Service Life of Working Layer for Ladle Furnace Designed by Changxing Refractory

Lalde furnace has been widely used in steel refining sector now, as a professional refractory manufacturer, Changxing Refractory has made lots of researches with the purpose of prolonging the service life of ladle furnace for our clients’. Now we would like to share our design for ladles working layer and corresponding service life based on our practical experience.?

The ladle furnace is divided into two types: Non-refining and Refining ladle according to the different output of steel product.?

1.?Non refining ladle, which is mainly applied for carbon steel.?

A. 50-80 heats. Using Alumina-magnesia Spinel brick as working layer. This proposal is specially applied for Ladle with the capacity of less than 50 Tons.?
B. 80-120 heats. Using?Magnesia Alumina Carbon brick?and?Magnesia Carbon brick?.?
C. 80-130 heats. Using Magnesia-magnesia spinel castable.?

2.?Refining ladle, it is mainly applied for producing higher standard steel. Such as alloy steel, stainless steel.?

A. 50-100 heats (Alloy steel application). Using?Magnesia Alumina Carbon brick?, Alumina Magnesia Carbon brick andMagnesia Carbon brick?.?
B. Stainless steel application.
a) 25-35 heats. Using?Low Carbon brick.?
b) 60-90 heats. Using Magnesia Calcium brick or Magnesia Calcium Carbon brick.
c) 120-160 heats. Using Corundum Spinel Castables and prefabricated impact plate at the bottom + Carbon free prefabricated plate at the wall +?Magnesia Carbon brick?at slag line area.??

The aforementioned proposals are actual feedbacks from our clients. It could be variable as per the different production process and refining period. So just tell us your current working situation and capacity of your ladle, Changxing engineers will customized the suitable design for you. With more than 30 years’ experience in refractory sector, Changxing is also available for whole design proposal for EAF, Tundish and Induction furnace etc. Here we are warmly welcome your inquiry or any other technical questions.
The link :http://www.chinafirebrick.com/Company_News_45.html