Construction of fire plastic material

The construction quality of fire plastic refractory raw material affects the service life of the furnace directly. When doing construction on the top of the furnace, if the construction is improper, accidents such as roof vault or roof collapse will occur. Therefore, fire plastics refractory raw material must be constructed as follows:

1.Combining fire plastic material and anchor bricks;

2.When the first layer of refractory raw material is hammered, shave the surface of plastic material with a scraper so that the bonding surface is rough; then place the second layer of plastic material and hammered in the same way;

3.Cut the expansion joint according to the design requirements;

4.Lay holes in the plastic refractory raw material after construction.

Changxing refractory provides refractory products, calcium silicate products, castable & mortar, china refractory brick, ceramic fiber felt, ladle & tundish nozzle, ceramic fiber with high quality for you. Such as high alumina refractory bricks, magnesia carbon brick, clay refractory bricks and other refractory products.

Article Source：Construction of fire plastic material
Company name: Henan Xinmi Changxing Refractory Materials Co.,Ltd
Email: sales1@chinafirebrick.com
Website:http://www.chinafirebrick.com/

Introduction of magnesia-calcium bricks

The magnesia-calcium brick, also known as high calcium magnesite brick, is a kind of magnesial refractory material with periclase as principal crystalline phase and tricalcium silicate as secondary phase. It contains 80 % ~ 87% MgO, 6 % ~ 9% CaO, CaO/SiO2 ratio is between 2.2 ~ 3.0. Its significant structural feature is periclase directly contact with dicalcium silicate and tricalcium silicate, making eutectic solution-4 Cao-Al2O3-Fe2O3 fill into crystal gap between dicalcium silicate and tricalcium silicate. Its porosity is low, the refractoriness under load is higher than 1700 ℃. It has good alkaline slag resistance ability, but with poor thermal shock resistance. Made by calcium magnesia sand as refractory raw material, it will be made by firing at 1550~1600 ℃ after crushing, burdening, mixing and molding. It will be used at eye place of side-blown converter, top place of open-hearth furnace and oxygen-blown converter etc.

Magnesia-calcium brick has seven properties: High temperature resistance, slag resistance, spalling resistance, wear resistance, purifying molten steel and hydration resistance performance.

With the increasing production of stainless steel and all kinds of clean steel products, the demand of various magnesia calcium brick are increasing accordingly. For better production and using correctly, detailed understanding and learning of working performance and influencing factors of magnesia calcium bricks are very necessary.

Changxing refractory provides refractory products, calcium silicate products, castable & mortar, china refractory brick, ceramic fiber felt, ladle & tundish nozzle, ceramic fiber with high quality for you. Such as high alumina refractory bricks, magnesia carbon brick, clay refractory bricks and other refractory products.

Article Source:Introduction of magnesia-calcium bricks
Company name: Henan Xinmi Changxing Refractory Materials Co.,Ltd
Email: sales1@chinafirebrick.com
Website:http://www.chinafirebrick.com/